Aperçu ProduitsZéolite ZSM-5

Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization

Je suis en ligne une discussion en ligne

Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization

Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization
Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization

Image Grand :  Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization

Détails sur le produit:
Lieu d'origine: La Chine
Nom de marque: QD
Certification: ISO9001:2015
Numéro de modèle: SiO2/Al2O3=10-1000
Conditions de paiement et expédition:
Quantité de commande min: 1 kilogramme
Prix: USD3000-10000 Ton
Détails d'emballage: 25kg/bags ou 500kg/bags et carbone
Délai de livraison: 5-8days
Capacité d'approvisionnement: 1000TON PAR MOIS

Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization

description de
Couleur: Blanc Rapport molaire: 15-1000
Forme nominale de cation: Ammonium/hydrogène PARI: 350-500m2/g
D'autres noms: ZSM-5 tamis moléculaire du zéolite hzsm-5 zsm-5 Application: Isomérisation de benzophénone

White Powder ZSM-5 Zeolite Molecular Sieve High Relative Crystallinity

 

Acid resistance

ZSM-5 zeolite has good acid resistance, it is resistant to various acids except hydrofluoric acid.

 

Mole Ratio: 15-1000
Nominal Cation Form: Ammonium/Hydrogen

 

Products

SiO2/Al2O3Mole Ratio Nominal Cation Form Na2O Weight % Surface Area, m2/g
QD 01 25 Sodium/Hydrogen 0.05 450
QD O2 30 Sodium/Hydrogen 0.05 450
QD 03 50 Sodium/Hydrogen 0.05 450
QD 04 80 Sodium/Hydrogen 0.05 450
QD 05 280 Sodium/Hydrogen 0.05 450

 

 

 

 

 

 

 

 

 

Na2O Weight %: 0.05
Surface Area, m2/g: 450

 

 

Description:

ZSM-5 zeolite properties

 

Thermal stability

High thermal stability of ZSM-5 zeolite. This is caused by a skeleton in a stable five-membered ring structure and a high silica to alumina ratio. For example, the sample calcined at 850 ℃ After 2 hours, the crystal structure unchanged. Even can withstand high temperature of 1100 ℃. So far, ZSM-5 zeolites are known to one of the highest qualitative hot temperature. Therefore, it is used in high-temperature process is particularly suitable. For example, use it as a hydrocarbon cracking catalyst, regeneration of the catalyst can withstand passage of time.

 

Steam stability

The studies have shown that when other zeolites by steam and hot water, and their general structure is destroyed, leading to irreversible deactivation. The Mobil company with ZSM-5 as the conversion of methanol (water is one of the major product) catalyst. This suggests that ZSM-5 to water vapor with good stability. 540 ℃ lower partial pressure of 22mmHg steaming column and HY zeolite HZSM-5 after 24 hours, a crystallinity of HZSM-5 and about 70 percent of fresh catalyst, but under the same conditions, HY zeolite skeleton almost completely damage.

 

Hydrophobic

ZSM-5 having a high silica to alumina ratio, the smaller the surface charge density. The water molecule is polar, so you will not ZSM-5 is adsorbed. Although water molecules smaller than the diameter of n-hexane, but the amount of adsorption of n-hexane ZSM-5 is generally greater than water.

 

Easy to coke

ZSM-5 V-shaped aperture effective, pore size and bending, preventing a large condensate formation and accumulation. Meanwhile, ZSM-5 framework is no greater than the bore of the cavity (cage) exist, so limiting the formation of large molecules from the secondary condensation reactions. So that the possibility of ZSM-5 catalyst coke is reduced. ZSM-5 for an alkyl aromatics into the tunnel barrier is formed, and thus the reaction process it can not continue to react in smaller pores, the final condensation formed coke. ZSM-5 so much slower than the rate of coke deposition and Y-type mordenite, difference of almost two orders of magnitude. Capacity of ZSM-5 zeolite carbon content is higher.

 

Excellent shape-selective selectivity

Zeolite molecular sieve as catalyst, only smaller than the hole crystal molecules can catalyze the reaction out of control pore size crystalline zeolite suffering zeolite catalyst size and shape of reactant and product molecules showed great selectivity. Pore ​​system of ZSM-5 zeolite having a 10-MR constituted medium size orifice diameter, it has a good shape-selective selectivity.

Synthetic Zeolite ZSM-5 Catalyst For Benzophenone Isomerization 0

Coordonnées
CATALYSTS GROUP CO.,LTD

Personne à contacter: Mr. Kevin

Téléphone: +8615666538082

Télécopieur: 86-533-52065599-2

Envoyez votre demande directement à nous (0 / 3000)